wood working and metal working strips
Grades selection
Tungsten carbide strips and plates are used for cutting metal, wood and other materials. The advantages of our carbide cutting strips and carbide cutting plates are smooth, fast cutting speed and have a long service time. Unlimited tracks of grades and sizes of carbide strips and carbide plates are available in our company. There are different grade for different working material, selection a suitable grade is very important!Cemented Carbide Bar Square Rod Tungsten Carbide Strips
Sample sizes of the tungsten carbide strips and plates
L | W | T | L | W | T | ||
200 | 200 | 1.5-65.0 | 120 | 120 | 1.5-65.0 | ||
200 | 150 | 1.5-65.0 | 120 | 100 | 1.5-65.0 | ||
200 | 120 | 1.5-65.0 | 120 | 80 | 1.5-65.0 | ||
200 | 100 | 1.5-65.0 | 120 | 50 | 1.5-65.0 | ||
200 | 80 | 1.5-65.0 | 100 | 80 | 1.5-65.0 | ||
150 | 150 | 1.5-65.0 | 100 | 50 | 1.5-65.0 | ||
150 | 120 | 1.5-65.0 | 80 | 80 | 1.5-65.0 | ||
150 | 100 | 1.5-65.0 | 80 | 60 | 1.5-65.0 | ||
150 | 80 | 1.5-65.0 | 60 | 60 | 1.5-65.0 | ||
150 | 50 | 1.5-65.0 | 50 | 50 | 1.5-65.0 | ||
… | … | … | … | … | … |
We produce tungsten strips and plates in different sizes and qualities. We accept orders of all Types of special products designed for our customers.
All our plate tungsten carbide products must be inspected strictly and only those without any damage, such as pores can be sent out.
Grade |
|
|
|
Performance & application recommended | |||||||
Density | T.R.S | Hardness | |||||||||
g/cm3 | MPα | HRA | |||||||||
YG6 | 14.9 | 2150 | 90.0 | Good wear resistance, used for hard wood, used for processing original wood, aluminum section bar, brass rod and cast iron. | |||||||
YG6A | 14.9 | 1860 | 92.0 | Has wear resistance higher than YG6, used for processing hard wood, original wood, aluminum section bar, brass rod and cast iron. | |||||||
YG8 | 14.7 | 2320 | 89.5 | Wear and percussion resistance , used for processing hard wood, soft wood, ferrous and non-ferrous. | |||||||
YS2T | 14.5 | 2350 | 92.0 | Fine carbide, High wear resistance, high bending strength, high resistance to bonding, high thermal strength. Machining of refractory alloys, stainless steel and high manganese steel, etc. | |||||||
YL10.2 | 14.5 | 3600 | 92.2 | Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous,metal and non-metallid materials. |